Anuwat Hassadee. Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 ferrite nanoparticles synthesized by co-precipitation method. (). King Mongkut's University of Technology North Bangkok. Central Library. : , 2017.
Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 ferrite nanoparticles synthesized by co-precipitation method
Name: Wimonrat Sapirach
Organization :
Bansomdejchaopraya Rajabhat University. Faculty of Education
Name: SupatraWongsa
Organization :
Bansomdejchaopraya Rajabhat University. Faculty of Education
Name: Anuwat Hassadee
Organization :
Bansomdejchaopraya Rajabhat University. Faculty of Science and Technology
Email :
anuwat8652@hotmail.com
keyword:
Co-precipitation method
LCSH:
Magnetic properties
Abstract:
Ni0.5Zn0.5Fe2O4 nanoparticles were prepared by co-precipitation method. The
chemical precursor for this work is Ni(NO3)2·6H2O, Zn(NO3)2·6H2O, Fe(NO3)3·9H2O and
NaOH solution (pH12 to pH14), after that calcined at 600oC for 2 h. The structure, sizes of
particles and magnetic properties of the samples were investigated by XRD, SEM and
VSM, respectively. The Ni0.5Zn0.5Fe2O4 nanoparticles have a cubic spinel structure at pH
12. At pH > 12 have composite of alpha Fe2O3 and cubic spinel Ni0.5Zn0.5Fe2O4 phase. The
average particles size was ~30 nm. The magnetization and coercivity of Ni0.5Zn0.5Fe2O4
nanoparticles are 18 emu/g and 2 Oe, respectively. VSM measurements indicated that the
samples were soft ferrite magnetic nanoparticles.The application of nanoparticles of Ni-Zn
ferrites using ferro-fluid, electronic device and cancer treatment in the future.
King Mongkut's University of Technology North Bangkok. Central Library
Address:
BANGKOK
Email:
library@kmutnb.ac.th
Created:
2017
Modified:
2562-08-14
Issued:
2019-08-14
บทความ/Article
application/pdf
BibliograpyCitation :
In Chemical Society of Thailand under the Patronage of Her Royal Hghness Princess Chulabhorn Mahidol and King Mongkut's University of Technology North Bangkok Faculty of Applied Science. Pure and Applied Chemistry International Conference (PACCON 2017) (pp.762-764). Bangkok : Chemical Society of Thailand under the Patronage of Her Royal Hghness Princess Chulabhorn Mahidol
eng
©copyrights King Mongkut's University of Technology North Bangkok
RightsAccess:
ใช้เวลา
0.03311 วินาที
Wimonrat Sapirach
| Title | Contributor | Type |
|---|---|---|
| Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 ferrite nanoparticles synthesized by co-precipitation method
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าพระนครเหนือ Wimonrat Sapirach;SupatraWongsa;Anuwat Hassadee | บทความ/Article |
SupatraWongsa
| Title | Contributor | Type |
|---|---|---|
| Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 ferrite nanoparticles synthesized by co-precipitation method
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าพระนครเหนือ Wimonrat Sapirach;SupatraWongsa;Anuwat Hassadee | บทความ/Article |
Anuwat Hassadee
| Title | Contributor | Type |
|---|---|---|
| อิทธิพลของการเติมสังกะสีที่มีผลต่อสมบัติทางไฟฟ้าและแม่เหล็กของ Co1-xZnxFe2O4 เฟอร์ไรท์
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี อนุวัฒน์ หัสดี;Anuwat Hassadee | วันดี อ่อนเรียบร้อย | วิทยานิพนธ์/Thesis |
| Structural and magnetic properties of Ni0.5Zn0.5Fe2O4 ferrite nanoparticles synthesized by co-precipitation method
มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าพระนครเหนือ Wimonrat Sapirach;SupatraWongsa;Anuwat Hassadee | บทความ/Article |