Metakaolinization effect on the thermal and physiochemical properties of Kankara kaolin

Name: Nurudeen Salahudeen

Organization : Bayero University

Email : nsalahudeen.cpe@buk.edu.ng

LCSH: KAOLIN -- THERMAL PROPERTIES

LCSH: KAOLINIZATION

ThaSH: CLAY MINERALS

Abstract: The effect of Metakaolinization on the thermal and physiochemical propperties of Kankara kaolin is presented. Thermogravimetric Analysis (TGA) and Differential Thermogravimetric (DTG) scan of Kankara kaolin indicated that kaolin was transformed to metakaolin at temperature above 600°C. The TGA/DTG scan of the metakaolin produced showed that the material was thermally stable at temperature range of 600–900°C. The metakaolin was characterized using X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Brunauer- Emmett-Teller (BET) texture analysis. The metakaolin formed was amorphous, having average particle size of 2.5 μm. The specific surface area values of the raw kaolin and the metakaolin formed were 12.95 and 19.38 m2/g respectively. The pore volume values of the raw kaolin and the metakaolin were 0.0038 and 0.0585 cm3/g respectively.

King Mongkut's University of Technology North Bangkok. Central Library

Address: Bangkok

Email: library@kmutnb.ac.th

Created: 2018

Modified: 2561-06-04

Issued: 2018-06-04

บทความ/Article

application/pdf

BibliograpyCitation : INTERNATIONAL JOURNAL OF APPLIED SCIENCE AND TECHNOLOGY. vol. 11, no. 2 (Apr.-June 2018), p. 127-135

eng

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	aij110206.pdf	939.97 KB

ใช้เวลา

0.018986 วินาที