การเตรียมและการศึกษาคุณสมบัติผิวเคลือบอะโนไดซ์แบบแข็งบนผิวรองรับ อะลูมิเนียม

Preparation and Evaluation of Hard Anodized Coating on Aluminium

Name: สมร หิรัญประดิษฐกุล

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

keyword: Hard anodizing

; Abrasion resistance

; อะโนไดซ์แบบแข็ง

; ค่าความต้านทานการเสียดสี

Abstract: Hard anodizing is an interesting industrial processes producing highabrasion resistant materials. Ahuninium oxide coated on the ahrminium has highhardness, high abrasion resistance, chemical and environment inertness leading tohigh corrosion resistance and excellent adhesion to the basis metaJs.The mainapplication of the coatings is in abrasion resistant coatings in aircraft industry andgeneral engineering. The general properties of this coating are as follows : hardnesshigher than 350 HV100 (Vic ers k microhardness tester) and thickness about 26-100 p. Thickness of anodized fihns for architectural work is about 16-30 Um.Anodizing converts ahuninium to ahuninium oxide having higherhardness. Oxide coating microstructures can be divided into two layers : an innerlayer is thin, compact and nonporous, called the barrier layer, and adheres to themetal surface, the outer layer, called the porous layer, is thicker than barrier layerand has a hexagonal cohmmar structun which is due to the dissolving action of theelectrolyte on individual cells formed at the pore bases.This research involved the study of hard anodizing process onahnninium. A gradient search technique was used to determine optimum hardanodizing condition, the objective function was maximum hardness. Relationshipbetween the hardness value of the surface and the abrasion resistance value wasdetermined. Tranmission and scanning electron microscopy techniques were usedto study the microstmctmes of hard anodized films.Four anodizing parameters were studied to be used follows : oxalic acidconcentration, ahuninium sulfate concentration, current density and anodizing time.Optimum condition was found to be as follows: oxalic acid concentration 7 5 g/l,ahminium sulfate concentration 75 g/l, current density 3.6 A/dm2, anodizingtime 90 mink The properties of the coating at this optimum condition was asfollowed : hardness value 453.1 HV100 , average thickness value 48.7 p andabrasion resistatux vahre 46.67 ds/mg when used Reciprocating Motion WearResistance TestThe abrasion resistance value of the hard anodized fihns varied directlywith the hardness vale. Thus, we could surmise that hard anodized fihns havinglarge hardness value would exhibit high abrasion resistant property.Scanning electron microscopy revealed the columnar microstructures ofthefilms.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: ดร. กฤษณพงศ์ กีรติกร,

Role: อาจารย์ที่ปรึกษา

Name: รศ.ดร. ศักรินทร์ ภูมิรัตน์

Role: อาจารย์ที่ปรึกษา

Created: 2537

Issued: 2005-04-15

Modified: 2006-05-30

วิทยานิพนธ์/Thesis

ISBN: 9746213148

CallNumber: CHE498

tha

DegreeName: วิศวกรรมศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: วิศวกรรมเคมี

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	CHE498.pdf	6.99 MB	244	2026-05-26 18:16:01
2	CHE498ab.pdf	128.72 KB	82	2026-05-26 18:16:01
3	CHE498ab.smi	2.64 KB	98	2026-05-26 18:16:01

ใช้เวลา

0.0435 วินาที