Actual chemical composition of phase diagram for blended cement paste

Name: Nichaphat Sitthisuk

Organization : Phranakhon Rajabhat University. Faculty of Industrial Technology

Name: Natt Makul

Organization : Phranakhon Rajabhat University. Faculty of Industrial Technology

Email : natt@pnru.ac.th

LCSH: Cement

LCSH: Phase diagrams

Abstract: This work focuses on studying the chemical composition of blended cement paste on the ternary phase diagram (TPD) of the CaO-AI2O3-SiO2 system hybridized to RSM-CCD. The heated curing was hydrated with ambient conditions. The samples were analyzed for chemical composition using the X-ray diffraction (XRD) technique, which led to the analysis of phase composition (metal-oxides contents; %w/w) using Chemix school v.12.5 software. Our results show that the hydrated cement induces the modification of the phase composition change as well as the hydration reaction of its solid compounds. The result shows that the thermal-assisted curing treatment under low conditions is significantly related to improved compression strength.

King Mongkut's University of Technology North Bangkok. Central Library

Address: BANGKOK

Email: library@kmutnb.ac.th

Created: 2567

Modified: 2024-07-30

Issued: 2024-07-30

บทความ/Article

application/pdf

BibliograpyCitation : ใน มหาวิทยาลัยธรรมศาสตร์ ศูนย์รังสิต. คณะวิศวกรรมศาสตร์. วิศวกรรมสถานแห่งประเทศไทย ในพระบรมราชูปถัมภ์. การประชุมวิชาการวิศวกรรมโยธาแห่งชาติ ครั้งที่ 29 : จากภูมิปัญญาที่สืบสานสู่การรังสรรค์โลกที่ยั่งยืน (NCCE 29) (MAT13). ปทุมธานี : มหาวิทยาลัยธรรมศาสตร์ ศูนย์รังสิต

eng

©copyrights King Mongkut's University of Technology North Bangkok

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	NCCE 29 MAT13.pdf	590.27 KB

ใช้เวลา

0.032007 วินาที