การแยกโลหะเงินจากน้ำล้างฟิล์มโดย Thiobacillus ferrooxidans DSM 583 และไคติน

Silver Recovery from Film Development Process Rinse Water by Thiobacillus ferrooxidans DSM 583 and Chitin

Name: สุภวัฒน์ เมฆสุต

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. คณะทรัพยากรชีวภาพและเทคโนโลยี. สาขาวิชาเทคโนโลยีชีวภาพ

keyword: เงิน

; การดูดซับ

; สารประกอบเชิงซ้อนซิลเวอร์ไทโอซัลเฟต

Abstract: Degradation of thiosulfate in film development process rinse water by Thiobacillus ferrooxidansDSM 583 and silver adsorption from film development process rinse water using chitin wereinvestigated in this study. Indirect method by using ~ ein ~oxi+dati on process was able to degrade0.01 M and 0.03 M of thiosulfate in sodium-thiosulfate solution within 2 and 5 days, respectively.However, 0.03 M of thiosulfate in film development process rinse water was rapidly degraded onlyin the first 3 days, and then the rate of degradation was declined due to buffer containing in filmdevelopment process rinse water. The buffer could maintain the pH of film development processrinse water to around 4.6 that was not the optimal pH for growth of Thiobacillus ferrooxidans DSM583. The pH adjustment to 2.8 by sulfuric acid was able to increase the percentage of thiosulfatedegradation, but the acid caused the precipitation of silver as silver sulfide. The silver in filmdevelopment process rinse water, [A~(s,o,),]-, was adsorbed by chitin after thiosulfate degradationstep. The results showed that F? and ~ ere~mai+nin g in the solution affected to decrease silveradsorption efficiency of chitin. Reducing of the inoculum size from 10% (vlv) to 2% and 0.5% (vlv)could not solve the problem. In addition, using sulfur as the substance instead of ferrous sulfateresulted to degrade 0.01 M thiosulfate of film development process rinse water only 20%, andsulfuric acid that is the product of degradation process induced silver precipitation. Accordingly,T. ferrooxidans DSM 583 could degrade thiosulfate in film development process rinse water byusing ferrous sulfate as substrate; however, the silver adsorption could be interfered by ~ ean~d ~+e ~ +remaining.The study of silver adsorption by chitin showed that silver-thiosulfate complex was completelyadsorbed within 10 minutes, and the optimal dosage was 6% (wlv). Silver adsorbed onto chitin waseluted by 1.0-4.0 M of sodium thiosulfate to 51-57%, respectively. The results of elution and FTIRspectra of chitin surface before and after silver adsorption indicated that the adsorption waschemical adsorption. The adsorption mechanism was proposed to be electrostatic attraction betweenprotonated amino group of chitin and negative charge of silver-thiosulfate complex.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. สำนักหอสมุด

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: ไพทิพย์ ธีรเวชญาณ

Role: อาจารย์ที่ปรึกษา

Name: วรนันต์ นาคบรรพต

Role: อาจารย์ที่ปรึกษา

Created: 2547

Issued: 2007-06-15

Modified: 2007-07-20

วิทยานิพนธ์/Thesis

ISBN: 9741842473

CallNumber: BIT512

tha

DegreeName: วิทยาศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: เทคโนโลยีชีวภาพ

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	BIT512.pdf	2.07 MB	158	2018-08-14 15:57:47
2	BIT512ab.pdf	58.38 KB	43	2018-08-14 15:58:32
3	BIT512.txt	2.68 KB	45	2018-08-14 15:59:20

ใช้เวลา

0.029279 วินาที