การศึกษากระบวนการผลิตและสมบัติของแผ่นฉนวนความร้อนจากชานอ้อย

Studies of Process and Properties of Thermal Insulation Boards Produced from Bagasse

Name: ประยูร สุรินทร์

Name: Prayoon Surin

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. คณะพลังงานสิ่งแวดล้อมและวัสดุ. สายวิชาเทคโนโลยีวัสดุ

keyword: Insulation Board for Baggesse

; แผ่นฉนวนความร้อนชานอ้อย

Abstract: This thesis involves the study of processes and properties of thermal insulation boards produced from bagasse. It clearly demonstrates a beneficial alternative of utilizing agricultural residues. Thermal insulation property of bagasse fiber is a result from its porosity and molecular Structures. In this research, thermal insulation boards were produced by hot-pressing pretreated bagasse fibers mixed with urea formaldehyde resin (EU-617 grade). The main objective of this study is to investigate optimum conditions for the production and observe, physical and mechanical properties of thermal insulation boards produced from bagasse. Results from the study indicated that boards could well be produced by hot- pressing pretreated bagasse fibers mixed with 8%, 12%, 25%, 33%, and 42% urea formaldehyde resin at the mould temperatures ranging between 150 ?C and 160 ?C for four m~nutes. It was found that these condition yielded maximum cross-linking of the resin for which an impact resistance was cons~dered. Thermal conductivity of the boards tested by means ASTM C-177 standard were found to be in the range of 0.0724 -0.0925 W/m ?K depending on density and urea formaldehyde resin content. It was also found that thermal conductivity tended to increase with density and resin content. Moreover, experimental test results of water absorption, thickness swelling and elongation impact resistance, modulus of elasticity, modulus of rapture and internal bonding suggested that, in addition to being a good thermal insulator, the boards with 25% and 33% resin content heving the density brtween 600 and 700 Kg/ m can be used as a medium density fiber board that complies with the TlSl 966-2533 standard.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี. สำนักหอสมุด

Address: กรุงเทพมหานคร

Email: info.lib@mail.kmutt.ac.th

Name: พัฒนะ รักความสุข

Role: อาจารย์ที่ปรึกษา

Created: 2544

Issued: 2007-01-19

Modified: 2007-03-12

วิทยานิพนธ์/Thesis

ISBN: 9746286439

CallNumber: MT117

tha

DegreeName: วิศวกรรมศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: เทคโนโลยีวัสดุ

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	MT117.pdf	5.49 MB
2	MT117ab.pdf	45.83 KB
3	MT117ab.txt	2.19 KB

ใช้เวลา

0.034033 วินาที