ผลกระทบของเส้นใยโพลีเอสเตอร์ที่มีต่อคุณสมบัติด้านวิศวกรรมของดินเหนียว

Effect of Polyester Fibers on Engineering Properties of Clay

Name: เอกรัตน์ รอดบำรุง

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

keyword: Fiber Reinforcement

; Cracking Test

Abstract: he engineering properties of polyester fibers and clay composite were evaluated by a series of laboratory unconfined-compression test, indirect tensile test, and cracking test. The inclusion of randomly distributed fibers significantly increased the peak compressive strength, ductility, and tensile strength of clay. The increase in strength was a function of fiber content. The result of the cracking test shows that effective in reducing the amount of desiccation cracking that occurs in clays subjected to drying. Therefore, mixture of 0.1 percent polyester fiber in clay will offer the optimum fiber content for reducing the amount of desiccation crack and practice. Mixing of fibers and clay is a critical factor in the case of randomly oriented fiber reinforcement. It was found to be very difficult to mix the fiber into the moist soil. The degree of randomness in the mixture was determined by visual inspection.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: มนตรี เดชาสกุลสม

Role: อาจารย์ที่ปรึกษา

Created: 2545

Issued: 2006-03-08

Modified: 2553-10-03

วิทยานิพนธ์/Thesis

ISBN: 9744562404

CallNumber: CVE1914

tha

DegreeName: วิศวกรรมศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: วิศวกรรมโยธา

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	CVE1914.pdf	5.07 MB	64	2021-11-26 16:30:36
2	CVE1914ab.pdf	71.22 KB	20	2019-07-27 19:55:22
3	CVE1914ab.txt	1.21 KB	16	2019-07-27 19:55:34

ใช้เวลา

0.033125 วินาที