การศึกษาเพื่อหาเกณฑ์ความเสียหายที่เหมาะสมที่สุดกับกระบวนการตัด

Investigation of the Most Appropriate Fracture Criterion in Blanking Process

Name: วีระชัย ลิ้มพรชัยเจริญ

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

Name: Weerachai Limpornchaijareorn

keyword: Fracture Criterion

; Blanking Process

; Cutting Clearance

; Fracture Initiation

Abstract: The purpose of this study is to investigate the most appropriate fracture criterion in Blanking Process . Blanking die was designed and manufactured to blank circular part of 25 mm diameter from stainless steel grade AISI 430 , low carbon steel (SPCC;JIS) , and aluminum (A1010-H12) of 0.5 mm thickness . The clearance between punch and die was set at 3 percent , 8 percent and 18 percent of sheet thickness . This work is carried out experimentally as well as FEM simulation (DEFORM 2D) . The positions of fracture initiation were compared . It was formed that Rice & Tracy and Oyane fracture criterion are the most appropriate fracture criterion in blanking process.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: ผศ.ดร. พงศ์พันธ์ แก้วตาทิพย์

Role: อาจารย์ที่ปรึกษา

Created: 2546

Issued: 2005-08-31

Modified: 2006-05-10

วิทยานิพนธ์/Thesis

ISBN: 9741837283

CallNumber: MEE15544

tha

DegreeName: วิศวกรรมศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: วิศวกรรมเครื่องกล

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	MEE1554.pdf	5.76 MB	74	2024-06-21 14:34:38
2	MEE1554ab.pdf	73.17 KB	15	2018-05-13 03:11:53
3	MEE1554ab.txt	1.03 KB	8	2018-05-13 03:11:54

ใช้เวลา

0.037879 วินาที