สมบัติของยางผสมระหว่างยางธรรมชาติกับ ทรานส์พอลิไอโซปรีนที่ผ่านการวัลคาไนซ์แล้ว

The Properties of Vulcanizats Prepared from natural Rubber Mixed with Trans-Polyisoprene

Name: ชาญพจน์ เชี่ยวนาวิน

Organization : มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

keyword: vulcanization

; Trans-polyisoprene

; วัลคาไนเซชัน

; ทรานส์พอลิไอโซปรีน

Abstract: The research involves the study of mechanical properties for vulcanizates of the mixturebetween natural rubber (NR) and synthetic trans-1,4-polyisoprene (TPI). It was found thatvulcanization system influenced on the properties of vulcanized product in which products fromNR, NR mixed with TPI (W!!(w/w)) and TPI alone had the best mechanical properties whenconventional system, semi-efficient and efficient vulcanization systems were appliedrespectively. Compression resistance property was also tested at 25% contraction of thespecimen. It was remarkable that rubber product mixed with TPI (3O%(w/w)) had bettercompression resistance than NR product and NR product mixed with TPI (2O%(w/w)) had thesame compression resistance as NR product. Compression resistance of TPI product was foundto be lower than NR product. The incorporation of carbon black into rubber product increasedtensile strength but decreased elongation at break. Elastic property of TPI product was observednot to be influenced by carbon black. In addition, TPI was found to increase hardness andabrasion resistance of rubber products. The effect of temperature on mechanical properties ofrubber product was also investigated. It was clear that TPI increases the stability of NR producttoward aging under both high and low temperatures but still maintained mechanical and dynamicproperties as well as heat build up of rubber product. On the other hand, TPI helped NR undergo easier processing since storage moduhts and loss moduhts were lower. Moreover, TPIresulted in longer scorch time of vulcanization reaction. It was also found that rate constant ofvulcanization reaction increased with vulcanization temperature. Activation energy of TPIcompound was found to be slightly higher than that of NR compound.

มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

Address: กรุงเทพมหานคร (Bangkok)

Email: info.lib@mail.kmutt.ac.th

Name: ผศ.ดร.เพลินพิศ บูชาธรรม

Role: อาจารย์ที่ปรึกษา

Created: 2540

Issued: 2005-04-15

Modified: 2006-05-30

วิทยานิพนธ์/Thesis

ISBN: 9746240773

CallNumber: CHM253

tha

DegreeName: วิทยาศาสตรมหาบัณฑิต

Level: ปริญญาโท

Descipline: เคมีอุตสาหกรรม

Grantor: มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

©copyrights มหาวิทยาลัยเทคโนโลยีพระจอมเกล้าธนบุรี

ลำดับที่.	ชื่อแฟ้มข้อมูล	ขนาดแฟ้มข้อมูล	จำนวนเข้าถึง	วัน-เวลาเข้าถึงล่าสุด
1	chm253.pdf	27.25 MB	123	2026-05-26 18:16:01
2	chm253ab.pdf	83.36 KB	54	2026-05-26 18:16:01
3	chm253ab.smi	2.09 KB	41	2026-05-26 18:16:01

ใช้เวลา

0.050799 วินาที